Marko Dunđer (Avtor), Tomaž Vuherer (Avtor), Ivan Samardžić (Avtor)

Povzetek

The paper presents impact energy results of thermal cycle simulated specimens of quenched and tempered fine grain structural steel S960QL. These results are obtained by examining notched Charpy specimens. Upon performed metallographic analysis and measured hardness, total impact energy is separated into ductile and brittle components.

Ključne besede

kaljeno jeklo;popuščano jeklo;toplotna obdelava;udarna energija;čas ohlajanja;preiskava materiala;quenched and tempered fine grain structural steel;welding thermal cycle;impact energy;cooling time t8/5;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
UDK: 621.74
COBISS: 17884182 Povezava se bo odprla v novem oknu
ISSN: 0543-5846
Št. ogledov: 795
Št. prenosov: 104
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: kaljeno jeklo;popuščano jeklo;toplotna obdelava;udarna energija;čas ohlajanja;preiskava materiala;
URN: URN:SI:UM:
Vrsta dela (COBISS): Znanstveno delo
Strani: str. 637-640
Letnik: ǂVol. ǂ53
Zvezek: ǂno. ǂ4
Čas izdaje: 2014
ID: 10846219