Povzetek

This paper elaborates results of hardness and impact energy of thermal cycle simulated specimens of high-alloy steel P 91 and their dependence on cooling time from 800 to 500 °C. Results were obtained by measuring hardness HV 1 and by experimental testing of Charpy notched specimens. Metallographic analysis of samples was performed on scanning electronic microscope.

Ključne besede

varjenje;P 91;trdota;udarna energija;hlajenje;welding;hardness;impact energy;cooling;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
UDK: 621.791.052:669.15
COBISS: 18359062 Povezava se bo odprla v novem oknu
ISSN: 0543-5846
Št. ogledov: 1788
Št. prenosov: 82
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: varjenje;P 91;trdota;udarna energija;hlajenje;
URN: URN:SI:UM:
Vrsta dela (COBISS): Znanstveno delo
Strani: str. 539-542
Letnik: ǂVol. ǂ54
Zvezek: ǂiss. ǂ3
Čas izdaje: 2015
ID: 9142059