diplomsko delo
Aljoša Radić (Avtor), Borut Kosec (Mentor)

Povzetek

V diplomski nalogi je predstavljen postopek toplotne obdelave nerjavne debele pločevine, ki je bila izvedena v obratu Predelava debele pločevine, podjetja SIJ Acroni d.o.o. Opisani so postopki raztopnega žarjenja in gašenja na linji za toplotno obdelavo »Bellman«, s posebnim poudarkom na 3 conski komorni peči, ki je sestavni del v linije. V eksperimentalnem delu, so bile v prvi fazi v 3 conski komorni peči na proizvodni liniji za toplotno obdelavo, neposredno v industrijskem okolju izvedene meritve temperatur ter določen temperaturni profil plošče in peči ter temperaturni profil ohlajanja plošče s temperature raztopnega žarjenja. V nadaljevanju eksperimentalnega dela, so bile na podlagi krivulj določena temperaturna odstopanja ter določeni časi ogrevanja. Tako pridobljeni podatki so se nato uporabili za izvedbo pogojev raztopnega žarjenja oziroma toplotne obdelave na nerjavnih plošč iz jekla 316L (W.r. 1.4404) iz proizvodnega programa. Skladno s tem, je sledila analiza mehanskih in metalografskih lastnosti na katerih smo analizirali uspešnost toplotne obdelave.

Ključne besede

nerjavna debela pločevina;raztopno žarjenje;gašenje;toplotna obdelava;3 conska komorna peč;temperaturni profil;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL NTF - Naravoslovnotehniška fakulteta
Založnik: [A. Radić]
UDK: 669.1
COBISS: 1698399 Povezava se bo odprla v novem oknu
Št. ogledov: 1086
Št. prenosov: 386
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Heating of heavy steel plates in three zone gas chamber furnace
Sekundarni povzetek: Diploma thesis describes the process of heat treatment of stainless steel heavy plates, which was carried out at the steel factory SIJ Acroni d.o.o. The methods of solution annealing and quenching on the Bellman heat treatment line are described, with special emphasis on the three zone chamber furnace, which is located in the line. In the first phase of the experimental part, we performed temperature measurements in the three zone chamber furnace on the production line for heat treatment and determined the temperature profile of the plate and the furnace, and the temperature profile of cooling the plate from the temperature of the solution annealing. In second part of the experimental work, we measured temperature deviations and certain times of heating on the basis of the curves. The data thus obtained were then used to perform the conditions of the solution annealing or heat treatment on stainless steel 316L plates (w.r. 1.4404) from the production program. Accordingly, an analysis of the mechanical and metallographic properties was followed, in which the performance of the heat treatment was analyzed.
Sekundarne ključne besede: stainless heavy plates;solution annealing;quenching;heat treatment;3-zone chamber furnace;temperature analysis;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Komentar na gradivo: Univ. Ljubljana, Naravoslovnotehniška fak., Oddelek za materiale in metalurgijo