Dupleksna in superdupleksna jekla blagovne znamke Sinoxx 4462 in Sinoxx 4410 največjega slovenskega proizvajalca jekla SIJ ACRONI d.o.o. spadajo v skupino nerjavnih jekel, ki vsebujejo več kot 20 mas.% kroma. Zanje je značilna dvojna, tako imenovana dupleksna mikrostruktura, ki je pri sobni temperaturi sestavljena iz ferita s centrirano kubinčno kristalno mrežo in avstenita s ploskovno centrirano kubično mrežo. V diplomski nalogi je predstavljena analiza in optimizacija poteka temperaturnega profila debele jeklene pločevine in visokotemperaturne peči HTF (visokotemperaturna valjčna peč) na liniji HTL. Meritve temperaturnega profila so se izvedle neposredno v industrijskem okolju in sicer na 10 mm jekleni debelin pločevini vrste S32750, Wr. Nr. 1.4410, EN X2CrNiMo – 25 – 7 – 4 in 50 mm jekleni debeli pločevini vrste S32205, Wr. Nr. 1.4462, EN X2CrNiMoN – 22 – 5 – 3. V okviru dela smo na napravi za določevanje toplotnih lastnosti Hot Disk TPS 2200 izvedli meritve toplotne prevodnosti in specifične toplote in izračunali temperaturno prevodnost obeh kvalitet jekel v skladu s standardom ISO 22007-2.

Ključne besede

Sinoxx;dupleks nerjavno jeklo;superdupleks nerjavno jeklo;linija HTL (Heat treatment line);jeklena debela pločevina;visokotemperaturna peč HTF;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL NTF - Naravoslovnotehniška fakulteta
Založnik: [D. Zgonc]
UDK: 669
COBISS: 31692547 Povezava se bo odprla v novem oknu
Št. ogledov: 437
Št. prenosov: 124
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: heat treatment optimisation of heavy plattes from stainless steels
Sekundarni povzetek: Sinoxx 4462 duplex and Sinoxx 4410 super duplex steels are steels manufactured by the largest Slovenian steel manufacturer SIJ ACRONI Ltd. They are stainless steels, which means that the mass fraction of chromium always exceeds 20% in their composition. They are distinguished by their dual (duplex) microstructure comprised at room temperature of body-centered cubic lattice (BCC) ferrite and face-centered cubic lattice (FCC) austenite. This thesis is primarily concerned with analyzing and optimizing the temperature profile of steel heavy plattes and hight temperature furnace HTF on a heat treatment line HTL. Temperature profile was measured in an industrial enviroment containing a heat treatment line course of 50 mm duplex heavy plattes type S32205, Wr. Nr. 1.4462, EN X2CrNiMoN – 22 – 5 – 3 and 10 mm super duplex stainless steel heavy plates type S32750, Wr.Nr. 1.4410, EN X2CrNi – 22 – 5 – 3. Experimental research on heat property identification machine Hot Disk TPS 2200 enabled measuring heat conductivity and specific heat as well as calculating the conductivity of mender quality and prime quality steels in accordance with ISO 22007-2.
Sekundarne ključne besede: Sinoxx;duplex stainless steel;superduplex stainless steel;HTL line (heat treatment line);steel heavy plattes;hight temperature furnace HTF;
Vrsta dela (COBISS): Višješolska diplomska naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Strani: XIV, 86 f.
ID: 12031163