Stainless steels are widely used in industrial assets and equipment. Despite their good corrosion resistance under a wide range of operating conditions, there is the possibility of pitting corrosion in the presence of chlorides. However, very few studies have identified the safe operating conditions for various high-alloyed stainless steel grades by comparing their pitting susceptibility. In this research, the susceptibility to pitting attack of five stainless steels with austenitic and duplex microstructures was examined in dilute sulphuric acid solution with varying amounts of NaCl at the temperatures of 50, 90 and 130◦C. Based on potentiodynamic polarization scans, none of the test materials underwent pitting corrosion at 50◦C, but differences in susceptibility to pitting attack were clear between the test materials and NaCl concentrations at the temperature of 90◦C, and further tem- perature increase facilitated uniform corrosion. 28-day immersion tests at 90◦ C confirmed the pitting suscepti- bility of duplex grades 1.4662 (PREN 33) and 1.4462 (PREN 35) in the presence of at least 2000 mg/L NaCl, but not the susceptibility of a corresponding austenitic grade 1.4539 (PREN 34). The grades 1.4547 (PREN 43) and 1.4410 (PREN 44) were not susceptible to pitting corrosion under any of the studied conditions. The results from materials microstructural and electrochemical characterization are presented and discussed in this paper.

Ključne besede

nerjavno jeklo;avstenitno nerjavno jeklo;dupleks nerjavno jeklo;luknjičasta korozija;stainless steel;austenitic stainless steel;duplex stainless steel;pitting atttack;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: ZAG - Zavod za gradbeništvo Slovenije
Založnik: Elsevier
UDK: 544.5/.6
COBISS: 149437699 Povezava se bo odprla v novem oknu
ISSN: 1873-3859
Št. ogledov: 5
Št. prenosov: 2
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: nerjavno jeklo;avstenitno nerjavno jeklo;dupleks nerjavno jeklo;luknjičasta korozija;
Komentar vira: Nasl. z nasl. zaslona; Opis vira z dne 6. 6. 2023;
Strani: str. 1-28
Letnik: ǂVol. ǂ457
Zvezek: [article no.] 142404
Čas izdaje: Jul. 2023
DOI: 10.1016/j.electacta.2023.142404
ID: 19534584
Priporočena dela:
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program