Ojačitev slojnatega furnirnega lesa (LVL)

magistrsko delo

Blaž Gošnjak (Avtor), Aleš Straže (Recenzent), Milan Šernek (Mentor)

Povzetek

Lepljeni konstrukcijski elementi iz lesa morajo imeti ustrezne mehanske lastnosti. Za širšo uporabo v praksi je aktualno tudi izboljšanje njihove upogibne trdnosti in togosti. V ta namen smo mehanske lastnosti slojnatega furnirnega lesa (LVL) izboljševali s sintetičnimi vlakni, ki smo jih dodajali v lepilne spoje. Pri preizkusih smo uporabili bukov furnir, poliuretansko lepilo ter epoksidno lepilo in sintetična vlakna. Ta so bila ogljikova, kevlarjeva ter steklena, ki smo dodajali v obliki pletene mreže v zunanja dva lepilna sloja LVL in jih zlepili v ploščo. To smo razžagali in dobili preizkušance, pri katerih smo ugotavljali modul elastičnosti z nedestruktivno in destruktivno metodo. Najprej smo pri preizkušancih merili hitrost preleta ultrazvoka, nato pa smo še statične meritve opravili s tritočkovnim upogibnim testom. Ugotovili smo, da se modul elastičnosti furnirnega lesa najbolj poveča z dodajanjem ogljikovih vlaken. Kombinacije lepila in vlaken so sicer različno vplivale na izboljšanje upogibne togosti in trdnosti LVL. Preizkušanci lepljeni s poliuretanskim lepilom so izkazovali boljše trdnostne lastnosti, kot preizkušanci lepljeni z epoksidnim lepilom. Večja kot je bila gramatura ojačitvenih vlaken, večja je bila tudi ojačitev preizkušanca pri posamezni vrsti vlaken.

Ključne besede

slojnat furnirni les;vlakna;epoksi;poliuretan;upogibna trdnost;modul elastičnosti;

Podatki

Jezik:	Slovenski jezik
Leto izida:	2019
Tipologija:	2.09 - Magistrsko delo
Organizacija:	UL BF - Biotehniška fakulteta
Založnik:	[B. Gošnjak]
UDK:	630832.286:630824.839
COBISS:	3065993
Št. ogledov:	552
Št. prenosov:	137
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Angleški jezik
Sekundarni naslov:	Reinforcement of laminated veneer lumber (LVL)
Sekundarni povzetek:	Glued structural elements of wood must have the appropriate mechanical properties. For wider application in practice, it is also important to improve their bending strength and rigidity. For this purpose, the mechanical properties of laminated veneer lumber (LVL) were improved with synthetic fibres, which were added into bonding layer of LVL. In the experiment, we used beech veneer, polyurethane and epoxy adhesives and synthetic fibres. We used carbon fibres, aramid and glass fibres. Reinforcement was added in the form of knitted nets in the two outer adhesives layers of the LVL and glued to the plate. The plate was then cut and experiments carried out to determine the modulus of elasticity using non-destructive and destructive methods. For the first technique we measured the speed of ultrasound along the specimens to determine dynamic modulus of elasticity, and followed by static mechanical three-point bending test. The greatest increase in the modulus of elasticity was achieved with adding of carbon fibres. The adhesive and fibre combinations have had different impacts on the improvements in bending stiffness and strength. The specimens glued with the polyurethane adhesive showed better strength properties than those made with epoxy adhesive. The more reinforcement fibres were used, the greater the stiffness of the tested specimens.
Sekundarne ključne besede:	laminated veneer lumber;fibre;epoxy;polyurethane;bending strength;modulus of elasticity;
Vrsta dela (COBISS):	Magistrsko delo/naloga
Študijski program:	0
Konec prepovedi (OpenAIRE):	1970-01-01
Komentar na gradivo:	Univ. v Ljubljani, Biotehniška fak., Oddelek za lesarstvo
Strani:	X, 49 f.
ID:	11162702