evaluation of water adsorption, mechanical and optical properties
Povzetek
The aimof this study was to develop composite films from cellulose, chitosan and polyvinyl alcohol to obtain environmentally friendly materials. Toughness, burst strength, distance to burst and water adsorption properties weremeasured and analysed as a function ofcellulose (3–5%), chitosan (0–1%) andpolyvinyl alcohol (0–4%) con- tents. Polynomial modelswere obtained. Light-barrier properties, transparency, morphology, structural and ther- mal analyses were assessed. Results showed that chitosan and polyvinyl alcohol enhanced the mechanical properties of cellulose-based films. Toughness values ranged from 0.47 to 8.01 MJ/m3, burst strength values ranged from 929 to 6291 g, distance to burst ranged from 1.25 to 2.52 mm and water adsorption values ranged from52.30 to 143.56%. Cellulose and chitosan improved the UV light protection effect ofthe films. However, PVA increased the transmittance meanwhile improved the film transparency. FT-IR and DSC showed an interaction between the components ofthe films. Results showed that it is feasible to obtain cellulose-chitosan-polyvinyl alcohol composite films with improvedmechanical properties, high capacity to adsorbwater, good barrier properties against UV radiations and adequate transparency value. These properties could be useful for potential packaging applications in the food industry or as a partial alternative to synthetic films
Ključne besede
regenerated cellulose;puncture test;water adsorption;
Podatki
Jezik: |
Angleški jezik |
Leto izida: |
2018 |
Tipologija: |
1.01 - Izvirni znanstveni članek |
Organizacija: |
UNG - Univerza v Novi Gorici |
UDK: |
54 |
COBISS: |
42614787
|
ISSN: |
0141-8130 |
Št. ogledov: |
1524 |
Št. prenosov: |
0 |
Ocena: |
0 (0 glasov) |
Metapodatki: |
|
Ostali podatki
URN: |
URN:SI:UNG |
Vrsta dela (COBISS): |
Delo ni kategorizirano |
Strani: |
str. 235-246 |
Zvezek: |
ǂVol. ǂ117 |
Čas izdaje: |
Oct. 2018 |
DOI: |
10.1016/j.ijbiomac.2018.05.148 |
ID: |
12256789 |