effect on mechanical properties and water vapour permeability
Patricia Cazón (Avtor), Manuel Vázquez (Avtor), Gonzalo Velazquez (Avtor)

Povzetek

Novel composite films were prepared by dissolving microcrystalline cellulose (3–5% w/w) in NaOH/urea solution, followed by coagulation in acetic acid solution. The regenerated cellulose films were immersed in chitosan-polyvinyl alcohol solutions at concentrations of 0–1% w/w and 0–4% w/w, respectively. Tensile strength, percentage of elongation at break, Young's modulus and water vapour permeability were measured to assess the effect of each compound on the mechanical and barrier properties. Polynomial models were obtained to evaluate the effect of the formulation on the measured properties. The microstructure was analysed by scanning electron microscopy. Results showed tensile strength values in the range 27.75–78.48 MPa, similar to usual synthetic polymer films. Percentage of elongation at break ranged from 0.98 to 12.82%, increasing when polyvinyl alcohol and chitosan increased. Young's modulus ranged from 2727.04 to 4217.25 MPa, showing higher values than pure chitosan and polyvinyl alcohol films. The highest value was reached combining cellulose and polyvinyl alcohol without chitosan. The water vapour permeability (1.78·10−11-4.24·10−11 g/m s Pa) showed 2 orders of magnitude higher than that of synthetic polymers, but lower than pure chitosan and polyvinyl alcohol films. Results showed that it is feasible to obtain cellulose-chitosan-polyvinyl alcohol composite films with improved mechanical properties and water vapour permeability.

Ključne besede

regenerated cellulose;tensile strength;elongation at break;Young's modulus;water vapour permeability;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UNG - Univerza v Novi Gorici
UDK: 54
COBISS: 42615811 Povezava se bo odprla v novem oknu
ISSN: 0142-9418
Št. ogledov: 1707
Št. prenosov: 0
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

URN: URN:SI:UNG
Vrsta dela (COBISS): Delo ni kategorizirano
Strani: str. 536-544
Zvezek: ǂVol. ǂ69
Čas izdaje: Aug. 2018
DOI: 10.1016/j.polymertesting.2018.06.016
ID: 12256790