zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
Jakob Šturm (Avtor), Zoran Bergant (Mentor)

Povzetek

V okviru zaključne naloge smo se seznanili s procesom vakuumske infuzije, ki ji sledi še obdelava v avtoklavu. Naš namen je bil določiti čim boljše izdelovalne parametre za doseganje dobrih mehanskih lastnosti kompozita. Glavni cilj naloge je bil določiti optimalno razmerje ogljikovih vlaken in epoksi smole ter opredeliti prispevek avtoklava na izboljšanje upogibne trdnosti tako izdelanega kompozitnega vzorca. Poleg tega smo z analizo mikroskopskih slik določili vpliv avtoklava na poroznost kompozita, tako na površini kot po preseku. Mehanske lastnosti smo preverjali s tritočkovnim upogibnim preizkusom. Z večanjem količine smole do določenega volumskega razmerja se po postopku vakuumske infuzije mehanske lastnosti kompozita izboljšujejo. Ob dodatni uporabi avtoklava pa je bila za doseg enakih mehanskih lastnosti kompozita potrebna manjša količina smole. Avtoklav je pozitivno vplival tudi na stopnjo poroznosti v kompozitu, saj jo je v primerjavi z vzorci, izdelanimi brez avtoklava, zmanjšal v vseh vzorcih.

Ključne besede

diplomske naloge;vakuumska infuzija;kompozit;ogljikova vlakna;epoksi smola;avtoklav;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [J. Šturm]
UDK: 621.9.04:678.058.4(043.2)
COBISS: 72916227 Povezava se bo odprla v novem oknu
Št. ogledov: 621
Št. prenosov: 77
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Influence of content of carbon fiber of composite and hardening of epoxy matrix within autoclave on quality of composite of vacuum infusion
Sekundarni povzetek: As part of the final task, we became acquainted with the process of vacuum infusion, followed by processing in autoclave. Our intention was to determine the best production parameters for the achievement of good mechanical properties of composite. The main objective of the task was to determine the optimal ratio of carbon fibre and epoxy resin and to define the contribution of the autoclave to improving the bending strength of the composite sample thus produced. In addition, microscopy was used to determine the impact of the autoclave on the porosity of composite, both on the surface and after the cross-section. Mechanical properties were checked by a three-point bending test. We found that by increasing the resin volume to a certain volume ratio after the vacuum infusion process, the mechanical properties of composite improved. However, when the autoclave was used, smaller amount of resin was required to achieve the same mechanical properties of the composite. Autoclave also had a positive effect on the porosity rate in the composite, as it decreased in all samples compared to samples manufactured without autoclave.
Sekundarne ključne besede: thesis;vacuum infusion;composite;carbon fibre;epoxy resin;autoclave;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XIV, 31 f.
ID: 13123204
Priporočena dela:
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo