zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
Miha Fabjan (Avtor), Roman Šturm (Mentor)

Povzetek

V zaključnem delu »Lasersko pretaljevanje površin ogljikovih jekel C15 in C45« je predstavljena metodologija eksperimenta in ovrednotenje dobljenih rezultatov mikrostruktur in mikrotrdote kot posledica laserskega pretaljevanja Nd:YAG laserja dveh ogljikovih jekel z oz. brez zaščitnega plina Ar. S pomočjo meritev globin in širin pretaljenega in toplotno vplivanega območja ter meritev mikrotrdot v pretaljenem, toplotno vplivanem območju in osnovnem materialu smo določili optimalne procesne parametre, katerih cilje je bil, da s procesom laserskega pretaljevanja čim bolj utrdimo material, hkrati pa imamo čim večjo učinkovitost. Na podlagi analize rezultatov mikrostruktur in mikrotrdot se je izkazalo, da smo pri danih konstantnih in spreminjajočih veličinah optimalen parameter obdelave pri C15 dobili pri uporabi energije žarka E = 13,7 J, pri C45 pa pri E = 11,9 J. Poleg omenjenih energij žarka smo imeli še konstantni parametre t = 8ms, f = 4 Hz, v = 1.5 mm/s in ?v_Ar = 2 l/min. Po ovrednotenju meritev smo lahko opazili, da je C45 veliko bolj primeren material za lasersko utrjevanje površin, saj se v primerjavi z C15 začne pretaljevati že pri manjših močeh, prav tako je to pretaljevanje in vnos toplote v material skozi celoten potek bilo intenzivnejše v globino materiala.

Ključne besede

diplomske naloge;ogljikovo jeklo C15;ogljikovo jeklo C45;lasersko pretaljevanje površine;mikrostrukture;mikrotrdota;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [M. Fabjan]
UDK: 621.9.048.7(043.2)
COBISS: 115357955 Povezava se bo odprla v novem oknu
Št. ogledov: 493
Št. prenosov: 278
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Laser surface remelting of carbon steel C15 and C45
Sekundarni povzetek: In final thesis »Laser surface remelting of carbon steel C15 and C45« are presented methodology of an experiment and evaluation of the obtained results of microstructures and microhardness as result of laser surface remelting with Nd:YAG laser of two carbon steels with or without Ar gas protection. With help of measuring depths,widths and microhardness of remelted and heat-affected area and base material, we determined the optimal process parameters, whose goals were to harden material as much as possible and while doing that, we also wanted the biggest efficiency Based on the analysis of the results of microstructures and microhardnesses, it turned out that for given constant and changing values, the optimal processing parameter for C15 was obtained when using the beam energy E = 13.7 J and for C45 at E = 11.9 J. Beside mentioned beam energies, we also had constant parameters like t = 8ms, f = 4 Hz, v = 1.5 mm/s and Φv_Ar = 2 l/min. After evaluating the measurements, we could see that C45 is a much more suitable material for laser hardening of surfaces as C15, since it begins to remelt at lower powers and in addition, also remelting and heat input into material throught the whole process is more intense to the depth of material.
Sekundarne ključne besede: thesis;carbon steel C15;carbon steel C45;laser surface remelting;microstructure;microhardness;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XIV, 39 f.
ID: 15907828
Priporočena dela:
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, ni podatka o podnaslovu
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo