Sinteza magnetnih nanodelcev za uporabo v biomedicini

diplomsko delo univerzitetnega študijskega programa I. stopnje

Karin Turner (Avtor), Irena Ban (Mentor), Janja Stergar (Komentor)

Povzetek

V sklopu diplomskega dela smo sintetizirali magnetne nanodelce z uporabo visokoenergetskega planetarnega mlina. Prah železa in bakra smo mleli v inertni in zračni atmosferi, pri čemer smo spreminjali čas mletja in sestavo vzorca. Namen diplomskega dela je bil raziskati ali lahko s pomočjo mletja sintetiziramo zlitino FeCu s Curiejevo temperaturo (T_C), ki bi bila znotraj terapevtskega območja za uporabo v magnetni hipertermiji (MH). Sintezo FeCu nanodelcev smo začeli z mletjem v zračni atmosferi. Spreminjali smo sestavo vzorca in podaljševali čas mletja. Vsem vzorcem smo s pomočjo modificirane termogravimetrične analize (TGA) izmerili T_C. Najboljši rezultat smo dobili po 25 urnem mletju vzorca s sestavo Fe_40 Cu_60, vendar so meritve T_C pokazale, da so v produktu prisotni železovi oksidi in nekaj nezreagiranega železa. Vzorec enake sestave mlet 20 h smo dodatno okarakterizirali z rentgensko praškovno difrakcijo (RTG), ki je potrdila, da med mletjem v zračni atmosferi prihaja do neželene oksidacije. Za primerjavo smo tri vzorce zmleli tudi v inertni atmosferi argona. Produkti, ki smo jih dobili niso vsebovali železovih oksidov, so pa vsebovali nezreagirano železo. Rezultati kažejo, da je za uspešno sintezo FeCu nanodelcev ključna inertna atmosfera. Glede na to, da je pri samem mletju ostalo še tudi nezreagirano železo bo v nadaljevanju potrebno razmišljati v smeri spreminjanja parametrov, ki bodo vodili v uporabo FeCu nanodelcev na področju MH.

Ključne besede

magnetni nanodelci;FeCu;mehansko mletje;biomedicinske aplikacije;magnetna hipertermija;diplomske naloge;

Podatki

Jezik:	Slovenski jezik
Leto izida:	2023
Tipologija:	2.11 - Diplomsko delo
Organizacija:	UM FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik:	[K. Turner]
UDK:	620.3:669.15.018.58(043.2)
COBISS:	148477955
Št. ogledov:	54
Št. prenosov:	18
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Angleški jezik
Sekundarni naslov:	Synthesis of magnetic nanoparticles for applications in biomedicine
Sekundarni povzetek:	As part of this thesis, we synthesised magnetic nanoparticles using a high-energy planetary mill. The iron and copper powders were milled in inert and air atmospheres, varying the milling time and sample composition. The aim of the thesis was to investigate whether milling could be used to synthesise a FeCu alloy with a Curie temperature (T_C) within the therapeutic range for applications in magnetic hyperthermia (MH). The synthesis of FeCu nanoparticles began by milling in an air atmosphere. We varied the composition of the sample and extended the milling time. The T_C was measured for all samples by modified thermogravimetric analysis (TGA). The best result was obtained after grinding a sample with composition Fe_40 Cu_60 for 25 hours, but the T_C measurements showed that iron oxides and some unreacted iron were present in the product. A sample of the same composition milled for 20 h was further characterised by X-ray powder diffraction (XRD), which confirmed that undesirable oxidation occurs during milling in an air atmosphere. For comparison, three samples were also ground in an inert argon atmosphere. The products we obtained did not contain iron oxides but did contain unreacted iron. The results show that an inert atmosphere is crucial for the successful synthesis of FeCu nanoparticles. Given that there is also unreacted iron left over from the milling process, further consideration will need to be given to changing the parameters that will lead to the use of FeCu nanoparticles in the MH field.
Sekundarne ključne besede:	magnetic nanoparticles;FeCu;mechanical milling;biomedical applications;magnetic hyperthermia;