Poly(glycidyl methacrylate-co-ethyleneglycol dimethacrylate) monolithic supports were prepared by radical polymerisation of the continuous phase of water in oil high internal phase emulsions. Morphology of monolithic materialswas studied by scanning electron microscopy and mercury intrusion porosimetry. The ratio of phase volume and the degree of crosslinking influenced the void size and pore size distribution of resulting polymers. Void sizes between 1 and 10 m were observed and average pore sizes around 100nm. Polymers with 60, 75, 80 and 90% pore volume were prepared and even samples with highest pore volume showed good mechanical stability. They were modified to bear weak-anion exchange groups and tested on the separation of standard protein mixture containing myoglobin, conalbumine and trypsin inhibitor. Good separation was obtained in a very short time similar to the separation obtained by commercial methacrylate monoliths. However, higher dispersion was observed. Bovine serum albumin dynamic binding capacity for monolith with 90% porosity was close to 9 mg/ml.

Ključne besede

organic chemistry;methacrylate monoliths;preparation;emulsion polymerisation;high porosity;high mechanical stability;polymer chromatographic supports;monolithic methacrylate supports;protein separation;polyHIPE;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FKKT - Fakulteta za kemijo in kemijsko tehnologijo
UDK: 547:678.7
COBISS: 9370134 Povezava se bo odprla v novem oknu
ISSN: 0021-9673
Št. ogledov: 1853
Št. prenosov: 45
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarne ključne besede: organska kemija;metakrilatni monoliti;priprava;emulzijska polimerizacija;visoka poroznost;visoka mehanska stabilnost;polimerni kromatografski nosilci;monolitni metakrilatni nosilci;separacija proteinov;
URN: URN:SI:UM:
Strani: str. 69-73
Letnik: ǂVol. ǂ1065
Zvezek: ǂiss. ǂ1
Čas izdaje: 2005
ID: 8718472