Sol-gel sinteza volframovih bronz (Na[spodaj]x WO[spodaj]3)

diplomsko delo

Aleš Rajbar (Avtor), Zoran Novak (Mentor), Željko Knez (Komentor)

Povzetek

S sol—gel sintezo smo pripravili bronze NaxWO3 z x=0,66. Bronze NaxWO3 so najpogosteje raziskovane in x ima razpon od 0 do vključno 1, zato imajo tudi velik obseg lastnosti, ki znajo biti koristne. Našli smo novo pot za pripravo čiste bronze, ki je enostavnejša, ker ni potrebno uporabiti visokih temperatur, zato pa so potrebne drage kemikalije in dobit produkta zaenkrat še ni ekonomična. Sinteza je bila izvedena po dveh poteh. Obe poti sta izvedeni po sol—gel metodi, ki zajema hidrolizo in kondenzacijo prej pripravljenega 5% prekurzorja WO(OEt)4, raztopljenega v EtOH. En način priprave je direktna pot, kjer dodamo Na+ z dodatkom NaOEt in nato poteče hidroliza. Na+ nam ni potrebno več dodati po hidrolizi, saj ga že imamo v raztopini. Drugi način priprave je preko WO3, kjer nastopi hidroliza prekurzorja WO(OEt)4 in nato vključitev Na+ v WO3. Po sintezi smo kserogele kalcinirali pri 850 in 600°C ter jih nato analizirali z RPD (rentgenska praškovna difrakcija), na podlagi katere smo lahko ugotovili njihovo čistoto oziroma uspešnost sinteze.

Ključne besede

natrij volframove bronze;volframati;sol-gel;kalciniranje;RPD;

Podatki

Jezik:	Slovenski jezik
Leto izida:	2009
Izvor:	Maribor
Tipologija:	2.11 - Diplomsko delo
Organizacija:	UM FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik:	[A. Rajbar]
UDK:	544.77.022.822:66.081(043.2)
COBISS:	13904406
Št. ogledov:	2189
Št. prenosov:	139
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Angleški jezik
Sekundarni naslov:	Sol-gel synthesis of tungsten bronzes (Na[sub]x WO[sub]3 )
Sekundarni povzetek:	Using sol-gel synthesis, tungsten bronzes NaxWO3 with x=0.66 have been prepared. Bronzes NaxWO3 are the most often researched ones with x ranging from 0 to 1 (including), that is also why they have a wide range of potentially useful properties. A way has been found to prepare pure bronze without high temperatures, simplifying the procedure, but it is currently not economically viable due to the costly chemicals that are required. The synthesis can be performed in two ways. Both employ the sol-gel method, which involves the hydrolysis and condensation of the ready-made 5% precursor WO(OEt)4 diluted in EtOH. One way is a direct one, whereby Na+ with the addition of NaOEt is added, whereupon hydrolysis takes place. The other way is via WO3, where hydrolysis takes place on the precursor WO(OEt)4, and then Na+ binds to WO3. After the synthesis, the xerogels have been calcinated at 800°C and 650°C, and then analyzed with XRD (X-ray diffraction), which allowed to determine their purity and thus the effectiveness of the synthesis.
Sekundarne ključne besede:	sodium tungsten bronze;tungstite;sol-gel;calcination;XRD;
URN:	URN:SI:UM:
Vrsta dela (COBISS):	Diplomsko delo
Komentar na gradivo:	Univ. v Mariboru, Fak. za kemijo in kemijsko tehnologijo
Strani:	35 f.
Ključne besede (UDK):	mathematics;natural sciences;naravoslovne vede;matematika;chemistry;crystallography;mineralogy;kemija;physical chemistry;fizikalna kemija;chemistry of surface phenomena and colloids;kemija površinskih pojavov in koloidov;applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;chemical technology;chemical and related industries;kemijska tehnologija;kemijske in sorodne industrije;physical and physicochemical operations and equipment;physical and physicochemical effects on chemical processes;fizikalne in fizikalno-kemijske operacije ter oprema;fizikalni in fizikalno-kemijski vplivi na kemijske procese;
ID:	987620