Strokovni članek
Oznake:
Ni-Cr-Fe alloy;stress corrosion cracking;nuclear power plant;repair;
In the early days of pressurized-water nuclear-power-plant design Ni-based alloys were selected because of their good mechanical properties and corrosion resistance. Alloy 600 was used for some reactor-coolant pressure-boundary components and Alloy 82/182 was used for welds. Industrial experience in ...
Leto:
2011
Vir:
dLib.si Digitalna knjižnica Slovenije
Pregledni znanstveni članek
Oznake:
electric arc furnace;chromium oxidation;foaming slag;slag reduction;stainless steel;
The oxidation of chromium during the elaboration of stainless steels occurs with oxygen in solution blown in the melt and with oxides in the slag. The loss of chromium during the steel bath processing increases the production costs and generates problems because of the high content of chromium oxide ...
Leto:
2007
Vir:
dLib.si Digitalna knjižnica Slovenije
Strokovni članek
Oznake:
kontinuirno litje;elektromagnetno mešanje;lite gredice;prečno/osno makroizcejanje;
Leto:
2003
Vir:
dLib.si Digitalna knjižnica Slovenije
Strokovni članek
Oznake:
stainless steel;SEM;cathodic protection;chlorination;pitting corrosion;crevice corrosion;
Equipment made from austenitic stainless steel corroded already after six months of the operation of an indoor marine-water basin. Two super chlorinations were performed during this period. Corroded stainless-steel components and different fastening components were investigated to detect the corrosi ...
Leto:
2012
Vir:
dLib.si Digitalna knjižnica Slovenije
Izvirni znanstveni članek
Oznake:
jekla;nekovinski vključki;kalcijev oksid;aluminijev oksid;
V članku izhajamo iz binarnega sistema CaO - ▫$Al_2O_3$▫, v katerem so vidne velike razlike v temperaturah tališč posameznih faz. Pri temperaturah obdelave tekočega jekla s kalcijem med 1550°C in 1650°C je tekoča faza v območju 12CaO . 7▫$Al_2O_3$▫. Za študij obnašanja kalcija in njegovega vpliva na ...
Leto:
1992
Vir:
dLib.si Digitalna knjižnica Slovenije
Pregledni znanstveni članek
Oznake:
austenitic stainless steels;continuous casting;solidification structure;intergranular cracks and voids;hot workability;effect of impurities;
A survey of the solidification structure of austenitic stainless steels is presented. The solidification occurs, depending on the content of the main alloying elements, with the primary formation of [delta]-ferrite or austenite. In the case of primary solidification of [delta]-ferrite, this phase re ...
Leto:
2006
Vir:
dLib.si Digitalna knjižnica Slovenije
Strokovni članek
Oznake:
blade;impeller;stainless steel;cast steel;crack;
The axial pumps are used in a wide variety of applications, such as drainage control, power plants and process cooling. A fresh-water, vertical, axial-pump, stainless-steel impeller failed. The impeller was a single cast from stainless steel. A visual examination indicated that the fracture originat ...
Leto:
2013
Vir:
dLib.si Digitalna knjižnica Slovenije
Izvirni znanstveni članek
Oznake:
kontinuirno litje;elektromagnetno mešanje;nekovinski vključki;
V podjetju Steel Štore za boljšo kakovost ultih gredic ulivajo talino jekla z elektromagnetnim mešanjem. Štiripolni dvofazni induktivni mešalniki so postavljeni tik pod kokilo. preiskave so pokazale, da se gredice, ulite z elektromagnetnim mešanjem taline, strjujejo bolj homogeno, imajo večje sredin ...
Leto:
2004
Vir:
dLib.si Digitalna knjižnica Slovenije
Strokovni članek
Oznake:
vroče preoblikovanje;avstenitna nerjavna jekla;žveplo;
Zaradi slabe razteznosti v vročem so avstenitna nerjavna jekla, legirana z žveplom, nagnjena k tvorbi površinskih razpok med vročim valjanjem. V zvezi s to problematiko je bila analizirana vrsta jekla SS2343, legiranega z žveplom, ki ga izdelujemo v Acroniju. Površinske razpoke, ki nastajajo med vro ...
Leto:
2004
Vir:
dLib.si Digitalna knjižnica Slovenije
Izvirni znanstveni članek
Oznake:
nerjavna jekla;tehnologija VOD;legiranje dušika;kinetika prenosa dušika v talino;ekonomski aspekti precesa legiranja dušika;
Leto:
2002
Vir:
dLib.si Digitalna knjižnica Slovenije