Degradation of a Ni-Cr-Fe alloy in a pressurised-water nuclear power plant
Roman Celin, Franc Tehovnik
Strokovni članek
Oznake: Ni-Cr-Fe alloy;stress corrosion cracking;nuclear power plant;repair;
In the early days of pressurized-water nuclear-power-plant design Ni-based alloys were selected because of their good mechanical properties and corrosion resistance. Alloy 600 was used for some reactor-coolant pressure-boundary components and Alloy 82/182 was used for welds. Industrial experience in ...
Leto: 2011 Vir: dLib.si Digitalna knjižnica Slovenije
A wet-steam pipeline fracture
Roman Celin, Dimitrij Kmetič
Strokovni članek
Oznake: pipeline;fracture;examination;fatigue failure;
The operational reliability of a system determines the systemćs availability and costs during its lifetime. Taking care of the reliability usually starts with knowledge of the operating conditions that need to be considered during the design, fabrication and maintenance of the system. In the case of ...
Leto: 2007 Vir: dLib.si Digitalna knjižnica Slovenije
Vpliv popravil na mikrostrukturo zvarov jekla Niomol 490K
Roman Celin, Janez Tušek
Strokovni članek
Oznake: varjenje;mikrostruktura;popravilo;toplotno vplivana cona;Niomol;
Pri varjenju jeklenih konstrukcij so pogosta popravila zvarjenih spojev zaradi odkritih, nedopustnih napak v zvaru. Še posebej so za varjenje zahtevna visokotrdnostna mikrolegirana drobnozrnata jekla. Opravljene so bile preiskave, ki naj bi pokazale, kako popravila zvara pri jeklu Niomol 490K vpliva ...
Leto: 2000 Vir: dLib.si Digitalna knjižnica Slovenije
A metallographic examination of a fractured connecting rod
Roman Celin, Boris Arzenšek, Dimitrij Kmetič
Strokovni članek
Oznake: connecting rod;nodular cast iron;failure;metallographic examinations;
The connecting rod converts the piston's reciprocating motion into the rotary motion of the crankshaft. During service, connecting rods are subjected to a various loads. In the case of the connecting rod investigated here, the failure occurred after just 20,000 km on the car's odometer (approximatel ...
Leto: 2008 Vir: dLib.si Digitalna knjižnica Slovenije
Kontrola rezervoarjev za naftne derivate
Roman Celin, Jelena Vojvodič-Tuma, Gorazd Kosec
Strokovni članek
Oznake: rezervoar;kontrola;korozija;
Skladiščenje in pretovor naftnih derivatov morata imeti minimalen vpliv na okolje. Novejši rezervoarji so zato izdelani z dvojnim plaščem, dvojnim dnom, plavajočo membrano, kupolasto streho in sodobno merilno regulacijsko opremo. Kljub upoštevanju predpisov in ukrepov za varno delo pa lahko pride do ...
Leto: 2004 Vir: dLib.si Digitalna knjižnica Slovenije
Impeller-blade failure analysis
Roman Celin, Franc Tehovnik, Franc Vodopivec, Borut Žužek
Strokovni članek
Oznake: blade;impeller;stainless steel;cast steel;crack;
The axial pumps are used in a wide variety of applications, such as drainage control, power plants and process cooling. A fresh-water, vertical, axial-pump, stainless-steel impeller failed. The impeller was a single cast from stainless steel. A visual examination indicated that the fracture originat ...
Leto: 2013 Vir: dLib.si Digitalna knjižnica Slovenije
Vizualna kontrola reaktorske glave v nuklearni elektrarni Krško
Roman Celin, Jelena Vojvodič-Tuma, Aleš Vučajnk, Vladimir Zado
Drugi članki ali sestavki
Oznake: reaktorska glava;vizualna kontrola;endoskop;
Leto: 2002 Vir: dLib.si Digitalna knjižnica Slovenije
Raziskave varjenja orodnega jekla
Roman Celin, Janez Tušek, Dimitrij Kmetič, Jelena Vojvodič-Tuma
Izvirni znanstveni članek
Oznake: varjenje;orodno jeklo;mikrotrdota;toplotna obdelava;
Predstavljena je analiza in primerjava različnih zvarjenih vzorcev orodnega jekla. Cilj analize vzorcev je bil poiskati optimalni postopek reparaturnega varjenja orodij za tlačno litje barvnih kovin. Pripravljene so bile tri serije vzorcev z različnim vnosom energije pri varjenju, različno toplotno ...
Leto: 2001 Vir: dLib.si Digitalna knjižnica Slovenije
Effect of change of carbide particles spacing and distribution on creep rate of martensite creep resistant steels
Danijela Anica Skobir Balantič, Monika Jenko, Franc Vodopivec, Roman Celin
Izvirni znanstveni članek
Oznake: creep resistant steel;creep rate;carbide particles;particles spacing;distribution of particles;tempered martensite;
The creep rate dependence of particles coarsening and spacing as well as distribution in analysed considering quoted equations. A simple method for assessment of particle spacing is proposed. Accelerated creep rates at 580 °C for CrV and CrVNb steel after different tempering times at 800 °C and 650 ...
Leto: 2011 Vir: dLib.si Digitalna knjižnica Slovenije
Revitalizacija zunanjega okrova visokotlačnega dela turbine 125 MW
Dimitrij Kmetič, Vinko Kurent, Ludvik Matko, Jerzy Dobosiewicz, Boris Arzenšek, Roman Celin
Strokovni članek
Oznake: okrov turbine;mikrostruktura;žilavost;neporušitvene preiskave;degradacija mehanskih lastnosti;revitalizacija;
Leto: 2002 Vir: dLib.si Digitalna knjižnica Slovenije
Št. zadetkov: 11
Ključne besede:
Leto izdaje:
Avtorji:
Repozitorij:
Tipologija:
Jezik: