Stress corrosion crack initiation testing with tapered specimens in high-temperature water - results of a collaborative research project
Rik-Wouter Bosch, Stefan Ritter, Matthias Herbst, Renate Kilian, Grace Burke, Jonathan Duff, Fabio Scenini, Yuchen Gu, Alice Dinu, Ulla Ehrnsten, Aki Toivonen, Radek Novotny, Oliver Martin, Francisco Javier Perosanz, Andraž Legat, Bojan Zajec
Izvirni znanstveni članek
Oznake: napetostno korozijsko pokanje;vpliv površinske obdelave;trapezast natezni vzorec;avtoklav;pospešeni test;lahkovodni jedrski reaktor;mejna napetost;stress corrosion cracking;surface finish impact;tapered tensile specimen;autoclave;accelerated testing;light water nuclear reactor;critical threshold stress;
The applicability of an accelerated test technique using tapered tensile specimens for investigating the stress corrosion crack (SCC) initiation behaviour of structural materials in high-temperature water was assessed in the framework of a European collaborative research project (MICRIN – MItigation ...
Leto: 2020 Vir: Zavod za gradbeništvo Slovenije (ZAG)