Investigation of surface treatment effects on the environmentally-assisted cracking behaviour of Alloy 182 in boiling water reactor environment
Zaiqing Que, Bojan Zajec, Stefan Ritter, Tommi Seppänen, Timo Saario, Aki Toivonen, Aleksandra Treichel, Valentin Lautaru, Fabio Scenini
Izvirni znanstveni članek
Oznake: iniciacija razpoke;pokanje zaradi vplivov okolja;zlitina Alloy 182;površinska obdelava;vrelovodni reaktor;odprti dostop;crack initiation;environmentally-assisted cracking;Alloy 182;surface machining;boiling water reactor;open access;
Surface treatments of primary circuit components in light water reactors are regarded as possible ways to mitigate environmentally-assisted cracking (EAC). To date, it is not fully conclusive which surface condition is suitable to reduce the EAC initiation susceptibility. Constant extension rate ten ...
Leto: 2022 Vir: Zavod za gradbeništvo Slovenije (ZAG)
Stress corrosion crack initiation testing with tapered specimens in high-temperature water - results of a collaborative research project
Rik-Wouter Bosch, Stefan Ritter, Matthias Herbst, Renate Kilian, Grace Burke, Jonathan Duff, Fabio Scenini, Yuchen Gu, Alice Dinu, Ulla Ehrnsten, Aki Toivonen, Radek Novotny, Oliver Martin, Francisco Javier Perosanz, Andraž Legat, Bojan Zajec
Izvirni znanstveni članek
Oznake: napetostno korozijsko pokanje;vpliv površinske obdelave;trapezast natezni vzorec;avtoklav;pospešeni test;lahkovodni jedrski reaktor;mejna napetost;stress corrosion cracking;surface finish impact;tapered tensile specimen;autoclave;accelerated testing;light water nuclear reactor;critical threshold stress;
The applicability of an accelerated test technique using tapered tensile specimens for investigating the stress corrosion crack (SCC) initiation behaviour of structural materials in high-temperature water was assessed in the framework of a European collaborative research project (MICRIN – MItigation ...
Leto: 2020 Vir: Zavod za gradbeništvo Slovenije (ZAG)
Effect of surface machining on the environmentally-assisted cracking of Alloy 182 and 316L stainless steel in light water reactor environments
Mariia Zimina, Stefan Ritter, Bojan Zajec, Marc Vankeerberghen, Liberato Volpe, Anna Hojna, Rik-Wouter Bosch, Fabio Scenini, Zaiqing Que, Alberto Sáez-Maderuelo, P. Jill Meadows, Michael Grimm, Matthias Herbst, Andraž Legat, Agostino Maurotto, Radek Novotny, Karl-Heinz Seifert
Izvirni znanstveni članek
Oznake: iniciacija razpoke;pokanje zaradi vplivov okolja;zlitina Alloy 182;avstenitno nerjavno jeklo AISI 304L;površina obdelave;lahkovodni reaktor;odprti dostop;crack initiation;environmentally-assisted cracking;Alloy 182;AISI 304 stainless steel;surface treatment;light water reactor;open access;
The main objective of the EU-funded project mitigating environmentally-assisted cracking through optimisation of surface condition (MEACTOS) was to gain knowledge on the ability of different surface machining procedures to mitigate environmentally-assisted cracking (EAC) in typical light water react ...
Leto: 2023 Vir: Zavod za gradbeništvo Slovenije (ZAG)