ǂThe ǂeffect of nitrogen-ion implantation on the corrosion resistance of titanium in comparison with oxygen- and argon-ion implantations
T. Sundararajan, Zdravko Praunseis
Izvirni znanstveni članek
Oznake: metalurgija;ionska implantacija;ortopedski implantati;korozija;titan;dušik;kisik;argon;metallurgy;ion implantation;orthopedic implants;corrosion;titanium;nitrogen;oxygen;
Commercially pure (CP) titanium was surface modified with nitrogen-, argon- and oxygen-ion implantations in order to investigate the material's corrosion resistance in a simulated body fluid. Five doses were chosen for the ions, ranging from 5.1015 cm-2 to 2.5-1017 cm-2. In-vitro open-cyclic potenti ...
Leto: 2004 Vir: Fakulteta za strojništvo (UM FS)